Water Based Hydroxyl Acrylic Resin
Water Dispersion Hydroxyl Acrylic Resin is two component PU resin, Reacted with polyisocyanate, through baking, it can maximize performance. water based hydroxyl acrylic dispersion can produce the same hardness, impact resistance and solvent resistance as solvent based polyurethane coating. coating made of these products is recommended to use in topcoat of metal or wood due to its paint film has excellent gloss, the construction method can be brushing, roll coating or spraying.
main features:
● Water dispersible type, emulsion form hydroxyl acrylic resin
● High solid content, low viscosity, low acid value
● Mixed with isocyanate cross-linking agent to be two component PU, has high gloss, high hardness
● Suitable for two component PU self-drying top coating and amino-baking top coatings
Polyurethanes have excellent chemical resistance. They are hard, tough finishes. They have chemical resistance, hardness & resilience for substrates ranging from plastics of all types to glass to wood to all metals, both primed & un-primed. These can either be polyurethane lacquers, oil-modified polyurethanes or two-component polyurethane systems.
Polyurethane materials are commonly formulated as paints and varnishes for finishing coats to protect. This use results in a hard, abrasion-resistant, and durable coating
Polyurethane varnish is capable of a much faster and higher "build" of film, accomplishing in two coats what may require many applications of oil. Polyurethane may also be applied over a straight oil finish, but because of the relatively slow curing time of oils, the presence of volatile byproducts of curing, and the need for extended exposure of the oil to oxygen, care must be taken that the oils are sufficiently cured to accept the polyurethane.
after evaporation of the solvent, upon reaction with oxygen from the air, polyurethane coatings cure after evaporation of the solvent by a variety of reactions of chemicals within the original mix, or by reaction with moisture from the air.
Our Waterborne Hydroxyl Acrylic Dispersion
| Product No. |
Type of polymer |
Solids content |
Viscosity
(25℃,mPa·s)
|
pH |
Neutral.agent |
OH value on solids
(mgKoH/g)
|
Air dry |
Cross-Linking
with amino resin
|
Grinding |
Property |
Application |
| WL-H152 |
Waterborne hydroxyl acrylic dispersion |
42±2 |
≤2000 |
7.0-8.0 |
DMEA |
116 |
●
(for 2K PU)
|
● |
● |
Good golss and DOI; Excellent flexibillity. |
2K PU topcoat |
| WL-157 |
Waterborne hydroxyl acrylic dispersion |
42±2 |
300-2000 |
7.0-8.0 |
DMEA |
115 |
●
(for 2K PU)
|
● |
● |
Quick-drying;
General-purpose product.
|
2K PU topcoat |
| WL-157A |
Waterborne hydroxyl acrylic dispersion |
47±2 |
300-2000 |
7.0-8.0 |
DMEA |
125 |
●
(for 2K PU)
|
● |
● |
Good golss; Good water resistance;
High limiting film thickness.
|
2K PU topcoat |
| WL-123A |
Waterborne hydroxyl acrylic dispersion |
44±2 |
300-2000 |
7.0-8.0 |
DMEA |
125 |
●
(for 2K PU)
|
● |
● |
Quick-drying; Good golss;
Excellent water resistance and chemical resistance.
|
2K PU topcoat |
PS:(1) The Viscosity with＊is measured in the case of the resin diluted by equivalent amount of propylene glycol methyl ethe-r.
(2) The symbol “●” means applicable. meanwhile, The symbol “○” means inapplicable.